Kondisyon Chimik
|
Eleman
|
Konpozisyon, %
|
|||||||
|
Kalite 1
|
Kalite 1b
|
Kalite 2
|
Kalite 2b
|
Kalite 3
|
Kalite 4
|
Kalite 5
|
Kalite 6
|
|
|
Kabòn, total, max
|
3.00 | 3.00 | 3.00 | 2.60 | 2.60 | 2.40 | 2.40 | 3.00 |
|
Silisyòm
|
1.00-2.80 | 1.00-2.80 | 1.00-2.80 | 1.00-2.80 | 1.00-2.00 | 5.00-6.00 | 1.00-2.00 | 1.50-2.50 |
|
Manganèz
|
0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 |
|
Nikèl
|
13.50-17.50 | 13.50-17.50 | 18.00-22.00 | 18.00-22.00 | 28.00-32.00 | 29.00-32.00 | 34.00-36.00 | 18.00-22.00 |
|
Kwiv
|
5.50-7.50 | 5.50-7.50 | 0.50 max | 0.50 max | 0.50 max | 0.50 max | 0.50 max | 3.50-5.50 |
|
Kwòm
|
1.5-2.5 | 2.50-3.50 | 1.5-2.5 | 3.00-6.00A | 2.50-3.50 | 4.50-5.50 | 0.10 max | 1.00-2.00 |
|
Souf, max
|
0.12 | 0.12 | 0.12 | 0.12 | 0.12 | 0.12 | 0.12 | 0.12 |
|
Molybdène, max
|
... | ... | ... | ... | ... | ... | ... | 1.00 |
AKote kèk D' mande, ranje 3.00-4.00% Kwòm rekòmande.
Kondisyon mekanik
|
Kalite 1
|
Kalite 1b
|
Kalite 2
|
Kalite 2b
|
Kalite 3
|
Kalite 4
|
Kalite 5
|
Kalite 6
|
|
|
Fòs rupture, min, ksi (MPa)
|
25(172) | 30(207) | 25(172) | 30(207) | 25(172) | 25(172) | 20(138) | 25(172) |
|
Brinell dite (3000 kg)
|
131 183 | 149 212 | 118 174 | 171 248 | 118 159 | 149 212 | 99 124 | 124 174 |
|
Dimansyon
|
"Y" Gwosè Blòk
|
|||||
|
Pou Distribisyon nan epesè mwens
pase 1⁄2 pous (13 mm)
|
Pou Distribisyon nan epesè 1⁄2 pous.
(13 mm) jiska 1 1⁄2 pous (38 mm)
|
Pou Distribisyon nan epesè nan
1 1⁄2 pous (38 mm) ak Plis
|
||||
|
nan.
|
mm |
nan.
|
mm |
nan.
|
mm | |
| A |
1⁄2
|
13 | 1 | 25 | 3 | 75 |
| B | 1 5/8 | 40 | 2 1/8 | 54 | 5 | 125 |
| C | 2 | 50 | 3 | 75 | 4 | 100 |
| D | 4 | 100 | 6 | 150 | 8 | 200 |
| E | 7 | 175 | 7 | 175 | 7 | 175 |
|
approx
|
approx
|
approx
|
approx
|
approx
|
approx
|
|
REMAK1-1⁄16 pous.=1.6 mm; 1⁄8 pous.=3.2 mm.